Sputter deposition is a physical vapor deposition (PVD) method of thin film deposition by sputtering. This involves ejecting material from a "target" that is a source onto a "substrate" such as a silicon wafer. Resputtering is re-emission of the deposited material during the deposition process by ion or atom bombardment. Sputtered atoms ejected from the target have a wide energy distribution, typically up to tens of eV (100,000 K). The sputtered ions (typically only a small fraction of the ejected particles are ionized — on the order of 1%) can ballistically fly from the target in straight lines and impact energetically on the substrates or vacuum chamber (causing resputtering). Alternatively, at higher gas pressures, the ions collide with the gas atoms that act as a moderator and move diffusively, reaching the substrates or vacuum chamber wall and condensing after undergoing a random walk. The entire range from high-energy ballistic impact to low-energy thermalized motion is accessible by changing the background gas pressure. The sputtering gas is often an inert gas such as argon. For efficient momentum transfer, the atomic weight of the sputtering gas should be close to the atomic weight of the target, so for sputtering light elements neon is preferable, while for heavy elements krypton or xenon are used. Reactive gases can also be used to sputter compounds. The compound can be formed on the target surface, in-flight or on the substrate depending on the process parameters. The availability of many parameters that control sputter deposition make it a complex process, but also allow experts a large degree of control over the growth and microstructure of the film.

Uses of sputtering[edit]

Sputtering is used extensively in the semiconductor industry to deposit thin films of various materials in integrated circuit processing. Thin antireflection coatings on glass for optical applications are also deposited by sputtering. Because of the low substrate temperatures used, sputtering is an ideal method to deposit contact metals for thin-film transistors. Perhaps the most familiar products of sputtering are low-emissivity coatings on glass, used in double-pane window assemblies. The coating is a multilayer containing silver and metal oxides such as zinc oxide, tin oxide, or titanium dioxide. A large industry has developed around tool bit coating using sputtered nitrides, such as titanium nitride, creating the familiar gold colored hard coat. Sputtering is also used as the process to deposit the metal (e.g. aluminium) layer during the fabrication of CDs and DVDs.

Hard disk surfaces use sputtered CrOx and other sputtered materials. Sputtering is one of the main processes of manufacturing optical waveguides and is another way for making efficient photovoltaic solar cells.

Sputter deposition is used in the sputter coating of specimens for scanning electron microscopy.

Comparison with other deposition methods[edit]

A typical ring-geometry sputter target, here gold showing the cathode made of the material to be deposited, the anode counter-electrode and an outer ring meant to prevent sputtering of the hearth that holds the target.

An important advantage of sputter deposition is that even materials with very high melting points are easily sputtered while evaporation of these materials in a resistance evaporator or Knudsen cell is problematic or impossible. Sputter deposited films have a composition close to that of the source material. The difference is due to different elements spreading differently because of their different mass (light elements are deflected more easily by the gas) but this difference is constant. Sputtered films typically have a better adhesion on the substrate than evaporated films. A target contains a large amount of material and is maintenance free making the technique suited for ultrahigh vacuum applications. Sputtering sources contain no hot parts (to avoid heating they are typically water cooled) and are compatible with reactive gases such as oxygen. Sputtering can be performed top-down while evaporation must be performed bottom-up. Advanced processes such as epitaxial growth are possible.

Some disadvantages of the sputtering process are that the process is more difficult to combine with a lift-off for structuring the film. This is because the diffuse transport, characteristic of sputtering, makes a full shadow impossible. Thus, one cannot fully restrict where the atoms go, which can lead to contamination problems. Also, active control for layer-by-layer growth is difficult compared to pulsed laser deposition and inert sputtering gases are built into the growing film as impurities.

Types of sputter deposition[edit]

Magnetron sputtering source

Sputtering sources often employ magnetrons that utilize strong electric and magnetic fields to confine charged plasma particles close to the surface of the sputter target. In a magnetic field electrons follow helical paths around magnetic field lines undergoing more ionizing collisions with gaseous neutrals near the target surface than would otherwise occur. (As the target material is depleted, a "racetrack" erosion profile may appear on the surface of the target.) The sputter gas is typically an inert gas such as argon. The extra argon ions created as a result of these collisions leads to a higher deposition rate. It also means that the plasma can be sustained at a lower pressure. The sputtered atoms are neutrally charged and so are unaffected by the magnetic trap. Charge build-up on insulating targets can be avoided with the use of RF sputtering where the sign of the anode-cathode bias is varied at a high rate (commonly 13.56 MHz).[1] RF sputtering works well to produce highly insulating oxide films but with the added expense of RF power supplies and impedance matching networks. Stray magnetic fields leaking from ferromagnetic targets also disturb the sputtering process. Specially designed sputter guns with unusually strong permanent magnets must often be used in compensation.

Ion-beam sputtering[edit]

A magnetron sputter gun showing the target-mounting surface, the vacuum feedthrough, the power connector and the water lines. This design uses a disc target as opposed to the ring geometry illustrated above.

Ion-beam sputtering (IBS) is a method in which the target is external to the ion source. A source can work without any magnetic field like in a hot filament ionization gauge. In a Kaufman source ions are generated by collisions with electrons that are confined by a magnetic field as in a magnetron. They are then accelerated by the electric field emanating from a grid toward a target. As the ions leave the source they are neutralized by electrons from a second external filament. IBS has an advantage in that the energy and flux of ions can be controlled independently. Since the flux that strikes the target is composed of neutral atoms, either insulating or conducting targets can be sputtered. IBS has found application in the manufacture of thin-film heads for disk drives. A pressure gradient between the ion source and the sample chamber is generated by placing the gas inlet at the source and shooting through a tube into the sample chamber. This saves gas and reduces contamination in UHV applications. The principal drawback of IBS is the large amount of maintenance required to keep the ion source operating.[2]

Reactive sputtering[edit]

In reactive sputtering, the deposited film is formed by chemical reaction between the target material and a gas which is introduced into the vacuum chamber. Oxide and nitride films are often fabricated using reactive sputtering. The composition of the film can be controlled by varying the relative pressures of the inert and reactive gases. Film stoichiometry is an important parameter for optimizing functional properties like the stress in SiNx and the index of refraction of SiOx.

Ion-assisted deposition[edit]

In ion-assisted deposition (IAD), the substrate is exposed to a secondary ion beam operating at a lower power than the sputter gun. Usually a Kaufman source, like that used in IBS, supplies the secondary beam. IAD can be used to deposit carbon in diamond-like form on a substrate. Any carbon atoms landing on the substrate which fail to bond properly in the diamond crystal lattice will be knocked off by the secondary beam. NASA used this technique to experiment with depositing diamond films on turbine blades in the 1980s. IAS is used in other important industrial applications such as creating tetrahedral amorphous carbon surface coatings on hard disk platters and hard transition metal nitride coatings on medical implants.

Comparison of target utilization via HiTUS process - 95%

High-target-utilization sputtering[edit]

Sputtering may also be performed by remote generation of a high density plasma. The plasma is generated in a side chamber opening into the main process chamber, containing the target and the substrate to be coated. As the plasma is generated remotely, and not from the target itself (as in conventional magnetron sputtering), the ion current to the target is independent of the voltage applied to the target.

High-power impulse magnetron sputtering (HIPIMS)[edit]

HIPIMS is a method for physical vapor deposition of thin films which is based on magnetron sputter deposition. HIPIMS utilizes extremely high power densities of the order of kW/cm2 in short pulses (impulses) of tens of microseconds at low duty cycle of < 10%.

Gas flow sputtering[edit]

Gas flow sputtering makes use of the hollow cathode effect, the same effect by which hollow cathode lamps operate. In gas flow sputtering a working gas like argon is led through an opening in a metal subjected to a negative electrical potential.[3][4] Enhanced plasma densities occur in the hollow cathode, if the pressure in the chamber p and a characteristic dimension L of the hollow cathode obey the Paschen's law 0.5 Pa·m < p·L < 5 Pa·m. This causes a high flux of ions on the surrounding surfaces and a large sputter effect. The hollow-cathode based gas flow sputtering may thus be associated with large deposition rates up to values of a few µm/min.[5]

Structure and morphology[edit]

In 1974 J. A. Thornton applied the structure zone model for the description of thin film morphologies to sputter deposition. In a study on metallic layers prepared by DC sputtering,[6] he extended the structure zone concept initially introduced by Movchan and Demchishin for evaporated films.[7] Thornton introduced a further structure zone T, which was observed at low argon pressures and characterized by densely packed fibrous grains. The most important point of this extension was to emphasize the pressure p as a decisive process parameter. In particular, if hyperthermal techniques like sputtering etc. are used for the sublimation of source atoms, the pressure governs via the mean free path the energy distribution with which they impinge on the surface of the growing film. Next to the deposition temperature Td the chamber pressure or mean free path should thus always be specified when considering a deposition process.

Since sputter deposition belongs to the group of plasma-assisted processes, next to neutral atoms also charged species (like argon ions) hit the surface of the growing film, and this component may exert a large effect. Denoting the fluxes of the arriving ions and atoms by Ji and Ja, it turned out that the magnitude of the Ji/Ja ratio plays a decisive role on the microstructure and morphology obtained in the film.[8] The effect of ion bombardment may quantitatively be derived from structural parameters like preferred orientation of crystallites or texture and from the state of residual stress. It has been shown recently [9] that textures and residual stresses may arise in gas-flow sputtered Ti layers that compare to those obtained in macroscopic Ti work pieces subjected to a severe plastic deformation by shot peening.

See also[edit]


  1. ^ Ohring, Milton. Materials Science of Thin Films (2nd ed.). Academic Press. p. 215. 
  2. ^ Bernhard Wolf (1995). Handbook of ion sources. CRC Press. p. 222. ISBN 0-8493-2502-1. 
  3. ^ K. Ishii (1989). "High-rate low kinetic energy gas-flow-sputtering system". Journal of Vacuum Science and Technology A 7: 256–258. doi:10.1116/1.576129. 
  4. ^ T. Jung & A. Westphal (1991). "Zirconia thin film deposition on silicon by reactive gas flow sputtering: the influence of low energy particle bombardment". Mat. Sc. Eng. A 140: 528–533. doi:10.1016/0921-5093(91)90474-2. 
  5. ^ K. Ortner; M. Birkholz & T. Jung (2003). "Neue Entwicklungen beim Hohlkatoden-Gasflusssputtern". Vac. Praxis (in German) 15: 236–239. doi:10.1002/vipr.200300196. 
  6. ^ J.A. Thornton (1974). "Influence of apparatus geometry and deposition conditions on the structure and topography of thick sputtered coatings". Journal of Vacuum Science and Technology 11: 666–670. Bibcode:1974JVST...11..666T. doi:10.1116/1.1312732. 
  7. ^ B. A. Movchan & A. V. Demchishin (1969). "Study of the structure and properties of thick vacuum condensates of nickel, titanium, tungsten, aluminium oxide and zirconium dioxide". Phys. Met. Metallogr. 28: 83–90. 
  8. ^ H. Windischman (1992). "Intrinsic stress in sputter-deposited thin film". Crit. Rev. Sol. St. Mat. Sci. 17: 547. Bibcode:1992CRSSM..17..547W. doi:10.1080/10408439208244586. 
  9. ^ M. Birkholz; C. Genzel & T. Jung (2004). "X-ray diffraction study of residual stress and preferred orientation in thin titanium films subjected to a high ion flux during deposition". J. Appl. Phys. 96: 7202–7211. Bibcode:2004JAP....96.7202B. doi:10.1063/1.1814413. 

Further reading[edit]

External links[edit]

Original courtesy of Wikipedia: http://en.wikipedia.org/wiki/Sputter_deposition — Please support Wikipedia.
This page uses Creative Commons Licensed content from Wikipedia. A portion of the proceeds from advertising on Digplanet goes to supporting Wikipedia.
5613 videos foundNext > 

thin film preparation deposition Sputter H .flv

thin film preparation deposition Sputter H.

sputtering deposition animation

Physical vapor deposition by sputtering technique. E:Mail:info@thinfilmscience.com.

PVD RF Sputtering coating principle Magnetron Sputter Deposition Process Animation

http://www.perkin-elmer-sputter.com We have been focusing on providing solutions and enhancements to Perkin-Elmer Sputtering Systems including Perkin-Elmer PE 4400, PE 4410, PE 4450, PE 4480 ...

ingA company PVD Sputtering coating principle0602

Mod-01 Lec-18 Sputter Deposition of Nitride Coating

Technology of Surface Coating by Prof. A.K. Chattopadhyay,Department of Mechanical Engineering,IIT Kharagpur.For more details on NPTEL visit http://nptel.ac.in.

Mod-01 Lec-19 Sputter Deposition of Molybdenum Di Sulphide Coating

Technology of Surface Coating by Prof. A.K. Chattopadhyay,Department of Mechanical Engineering,IIT Kharagpur.For more details on NPTEL visit http://nptel.ac.in.

PVD Multilayer Sputter deposition process

A view into a SNS NanoGrowth dual target sputter process chamber whilst depositing a multi-layered structure on silicon.

Sputtering Deposition Systems -AccuSputter AW 4450 and Perkin-ELmer 4400 Series Sputter

http://www.allwin21.com/perkin-elmer-sputtering.asp sales@allwin21.com Allwin21 Corp. focuses on and professionally provides the following fully refurbished or rebuilt sputtering equipment...

Sputter Deposition Equipment Perkin-Elmer 4400 4410 4450 4480 CTI CRYO Pump

http://www.perkin-elmer-sputter.com/perkin-elmer-sputter-system-spare-parts.htm We provide most spare parts of Perkin ELmer PE4400 Perkin-ELmer 4410 ,Perkin-Elmer 4450,Perkin-Elmer 4480 Sputter...

Denton DV502A Sputter Deposition

Bid Service, LLC Video Demo\Walkaround Denton DV502A Sputter Deposition.

5613 videos foundNext > 

157 news items

Economic Times
Wed, 25 Mar 2015 22:37:30 -0700

First there was gigabyte. Then came terabytes which now grew to petabytes. And beyond that there are exabytes, zettabytes, yottabytes and... nothing else; there are no words to describe the amount of data larger than that. There is so much data stored ...

Independent Online

Independent Online
Mon, 02 Mar 2015 21:03:44 -0800

Sputter deposition is a physical vapour deposition method that works by ejecting material from a source on to a substrate such as the glass panels the Alberts method requires. The metallic alloys are then exposed to a mixture of gases under controlled ...
Wed, 11 Dec 2013 02:50:05 -0800

The construction does not have any elastomer seals and can be baked to 250°C. The feature of UHV compatibility enables ultra pure sputter deposition that eliminates unintentional oxidation and nitridation of materials. The CUSP sources have an ...


Tue, 10 Mar 2015 08:33:45 -0700

De 50 jaar oude magneettape-technologie gebruikt nu een vacuumvorm techniek met de naam 'sputter deposition'. Door ionen van argon op een polymeerfoliesubstraat te schieten maakt Sony een laag van magnetische kristallen. Die kristallen van 7,2 ...
Tue, 24 Feb 2015 15:37:30 -0800

NEW YORK, Feb. 24, 2015 /PRNewswire/ -- This report analyzes the worldwide markets for Thin Layer Deposition Equipment in US$ Million by the following Deposition Technologies: Physical Vapor Deposition (PVD), Chemical Vapor Deposition (CVD) ...
Chemistry World
Tue, 08 Jan 2008 00:00:00 -0800

The team, led by Tsukasa Torimoto at Nagoya University and Susumu Kuwabata at Osaka University in Japan, have used a process called sputter deposition to form bimetallic particles. The particles, which have applications in biosensors and as catalysts ...
Tue, 09 Dec 2014 08:00:22 -0800

The researchers created thin films of chromium oxide using a technique called sputter deposition. They were able to tune the resistance of the chromium oxide films by controlling the oxygen content of the films: the higher the oxygen content, the ...


Thu, 18 Dec 2014 01:27:28 -0800

Atomic layer deposition (ALD) enables controlled deposition of dielectric materials in complicated device structures. In order to satisfy the requirements of a broad range of devices and application fields that can benefit from these dielectric films ...

Oops, we seem to be having trouble contacting Twitter

Support Wikipedia

A portion of the proceeds from advertising on Digplanet goes to supporting Wikipedia. Please add your support for Wikipedia!

Searchlight Group

Digplanet also receives support from Searchlight Group. Visit Searchlight